聚乙撑二氧噻吩-聚(苯乙烯磺酸盐)

100

high-conductivity grade

Visual Light Transmission (VLT): ≥ 80%

dispersion

0.5-1 wt. % (PEDOT: PSS in water)

<200 Ω/sq (coating : 40μ wet, drying: 6 min 130℃)

2 - 3.5

≤70 mPa.s(20 ℃)

2-8℃

CC1=C2OCCOC2=C(C)S1.CCC(C3=CC=CC=C3)C.C[SO3-]

100 g in Sure/Seal™

Poly(3,4-ethylenedioxythiophene)-poly(styrenesulfonate) (PEDOT:PSS) is a conductive polymer that is formed by electropolymerizing 3,4-ethylenedioxythiophene in a solution of poly(styrenesulfonate) (PSS). PEDOT is doped with positive ions and PSS with negative ions. It is mainly used in organic electronics due to the properties, which include

• low band gap
• good optical properties
• high conductivity
• low redox potential
• easy processing
• tunable film forming ability

High-conductivity grade.

PEDOT:PSS can be used as an electrode material with high mobility for charge carriers. It can be used for a wide range of energy based applications such as organic photovoltaics (OPV), dye sensitized solar cells (DSSCs), organic light emitting diodes (OLEDs), supercapacitors and biomedical sensors.
Orgacon^™ S315 is ready-to-use and made with conductive polymer PEDOT:PSS. Typical application processes are slot die, Meyer bar and gravure coating. It is particularly designed for optimal properties on PET and meet the requirements of several transparent electrodes applications as alternative to ITO.

• ITO substitution coating.
• ITO-free OPV.

• Surface electrical resistance (SER) at 90% VLT* (visual light transmission): 125 Ω/square.

*Typical properties on PET with bar coater. Thermal cured at 130 ℃/ 6 min. VLT according to ASTM D 1003, excludes substrate.

• Stability ratio R/R_0 (500 hr at 60 ℃, 95% RH) : 1.3.

Orgacon is a trademark of Agfa-Gevaert N.V.