Titania paste, reflector

MFCD00011269

329768277

NA.23

Titania paste, the reflector is a precursor for titania, that forms a mesoporous light scattering layer on the fluorine doped tin oxide (FTO) substrates. It is used in a variety of electrochemical devices to improve electron mobility and power efficiency.

Light scattering titania paste can be coated on the primary transparent layer of TiO₂ to form a bilayered titanium film. It can be used as a negative electrode for dye sensitized solar cells (DSSCs).
Scattering Reflector Titania Paste can be used in conjunction with Transparent Titania Paste for enhanced DSSC performance in applications where transparency is not required.
Scattering Titania Paste contains highly dispersed anatase scattering particles (150nm to 250nm). This paste produces a non-active scattering layer when applied onto a pre-printed active layer.
After drying; this paste must be fired – together with the pre-printed active layers – at or above 500℃. This results in an opaque sintered layer; with a thickness of ~3μm for one printed layer; when using a 90T mesh screen.

Storage: Store in the dark at 20℃

Product of Greatcell Solar^® exclusive supplier of Sun2 products under license from EPFL.
Greatcell Solar^® is a registered trademark of Greatcell Solar
Greatcell Solar is a registered trademark of Greatcell Solar

Crystal Structure: > 99% anatase (analysis carried out on starting material, prior to paste manufacture)

100

paste (white)

20.0 wt. % (+/- 1.2 wt%)

150-250 nm (scatter)

15000-25000 mPa.s (Analysis carried out with 20mm 4 degree cone/plate; 40 s-1)

1S/2O.Ti

GWEVSGVZZGPLCZ-UHFFFAOYSA-N

5, 20 g in glass bottle

GHS07

Warning

H315 - H319

P264 - P280 - P302 + P352 - P305 + P351 + P338 - P332 + P313 - P337 + P313

Eye Irrit. 2 - Skin Irrit. 2

10 - Combustible liquids

WGK 1